Dielectric property of polycrystalline ZrO2substituted BaTi 2O5 prepared by arc-melting

Xin Yan Yue, Rong Tu, Takashi Goto

Research output: Contribution to journalArticle

11 Citations (Scopus)

Abstract

ZrO2 substituted polycrystalline BaTi2O5, Ba(Ti1-yZry)2O5, (BT2Z), was prepared by arc-melting and the dielectric property was investigated by AC impedance spectroscopy. The length of a-axis increased from 1.6895 to 1.6952nm and that of c-axis increased from 0.9411 to 0.9436nm with increasing y up to 0.06. The b-axis was almost independent of ZrO2 content. The solubility limit of ZrO2 (y) in BT2Z can be 0.06. BT 2Z had a strong b-axis orientation at y < 0.06. The permittivity of BT2Z at y = 0.005 showed the highest peak of 3050 at 725 K and the peak temperature decreased from 750 to 465 K with increasing y from 0 to 0.064. A relaxor-like frequency dependence of permittivity was observed at y > 0.06.

Original languageEnglish
Pages (from-to)120-124
Number of pages5
JournalMaterials Transactions
Volume49
Issue number1
DOIs
Publication statusPublished - 2008 Jan 1

Keywords

  • Arc-melting
  • BaTiO
  • Dielectric property
  • Polycrystals
  • ZrO

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Dielectric property of polycrystalline ZrO<sub>2</sub>substituted BaTi <sub>2</sub>O<sub>5</sub> prepared by arc-melting'. Together they form a unique fingerprint.

  • Cite this