Dielectric property of poly- and single-crystalline BaTi2O 5 co-substituted with SrO and ZrO2

Xin Yan Yue, Rong Tu, Takashi Goto

Research output: Contribution to journal › Article › peer-review

1 Citation (Scopus)

Abstract

Poly- and single-crystalline BaTi2O5 co-substituted with SrO and ZrO2, Ba0.99Sr0.01(T 1-xZrx)2O5 (BT2SZ) were prepared by arc-melting and floating-zone (FZ) melting, respectively. The specimens showed a significant (020) orientation. The highest permittivity of poly-crystalline BT2SZ was 3880 at x = 0.005 and that of single-crystal was 27000 at x = 0.005. The Curie temperature (Tc) of poly-crystals decreased from 750 to 640 K with increasing x from 0 to 0.026 and that of single-crystals decreased from 750 to 710 K with increasing x from 0 to 0.008. The highest remnant polarization of single crystalline BT2SZ was 7.8× 10-2 Cm-2 at x = 0.008, higher than that of the poly-crystal.

Original languageEnglish
Pages (from-to)217-220
Number of pages4
JournalKey Engineering Materials
Volume388
Publication statusPublished - 2009 Jan 1

Keywords

  • Arc-melting
  • BaTiO
  • Dielectric property
  • FZ melting
  • SrO
  • ZrO

ASJC Scopus subject areas

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Dielectric property of poly- and single-crystalline BaTi<sub>2</sub>O <sub>5</sub> co-substituted with SrO and ZrO<sub>2</sub>'. Together they form a unique fingerprint.

Cite this