Diamond Deposition on WC-Co Cemented Carbide by Means of Hot-Filament Method

Hisashi Suzuki, Hideaki Matsubara, Noritoshi Horie

Research output: Contribution to journalArticlepeer-review

23 Citations (Scopus)

Abstract

The diamond deposition on WC-Co alloy substrate was studied using so-called hot-filament method, according to the depositing conditions previously published. To clarify the phenomena, model experiments using the substrate of coarse WC-10%Co alloy, the surfaces of which were treated in different ways, were mainly conducted. The substrate temperature from 1073 to 1223 K was needed for the diamond deposition. The number of diamond particles increased, when the substrate surface was scratched, and it further increased when the surface was etched to some extent to remove the binder after the scratching. As for the etched substrate, diamonds deposited after several minutes of reaction time at the edge of WC particles or at the edge of scratches on the particles. The incubation period for diamond deposition was clearly observed for the non-etched substrate. The carbon absorption of binder and the graphite formation on binder during reacting were confirmed. It was demonstrated that the adhesion between diamond and substrate for the etched substrate was sufficient enough, in good contrast to the case of non-etched substrate. The mechanism of adhesion mentioned above was described.

Original languageEnglish
Pages (from-to)262-269
Number of pages8
Journaljournal of the japan society of powder and powder metallurgy
Volume33
Issue number5
DOIs
Publication statusPublished - 1986 Jan 1
Externally publishedYes

ASJC Scopus subject areas

  • Mechanical Engineering
  • Metals and Alloys
  • Industrial and Manufacturing Engineering
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Diamond Deposition on WC-Co Cemented Carbide by Means of Hot-Filament Method'. Together they form a unique fingerprint.

Cite this