Development of a method for CO2 solidification of glass and concrete waste composites

Lihui Liu, Toshiyuki Hashida, Satoshi Teramura, Kimitoshi Karino

Research output: Contribution to journalArticlepeer-review

4 Citations (Scopus)

Abstract

Composite materials heve been prepared using a CO2 solidification process from milling dust of autoclaved lightweight concrete (ALC; as matrix material), reinforced by addition of crushed glass (bottle) waste. The effect of varying glass collet size (0.08-5 mm) and glass volume (10-30%) on the fracture properties in the glass/ALC composite was examined by four point bending tests. For the glass/ALC composite cured under atmospheric conditions, we show, by conducting CO2 solidification experiments at different CO2 gas pressures (atmospheric, and 4-10 MPa), that the rate of reaction at the sample surface is faster under pressure, than under atmospheric conditions. At 4-10 MPa experimental conditions, a solidified 'reaction rim' is formed away from the sample surface characterized by the deposition of calcite, and a long internal fracture is created inside the sample, which reduces bending strength, although these characteristic features are not evident in samples cured at atmospheric conditions. Creation of the 'reaction rim' impedes further diffusion of CO2 into the sample. Our results indicated that the CO2 solidification of glass/ALC composite materials is best advanced under atmospheric conditions. The result also indicated that for < 0.5 mm cullet size, the bending strength is enhanced, without being detrimental to fracture characteristics. However, increasing size of the crushed glass cullet (0.5 mm-5 mm) reduced the strength of the solidified composite. The interface between the ALC powder matrix and glass cullet was weak, and a fraction glass cullets 0.08-0.5 mm size may be incorporated in the waste concrete matrix by as much as 30 vol%.

Original languageEnglish
Pages (from-to)357-361
Number of pages5
JournalJournal of the Ceramic Society of Japan
Volume111
Issue number1293
DOIs
Publication statusPublished - 2003 May

Keywords

  • CO diffusion
  • CO-solidification
  • Composite
  • Fracture properties
  • Waste concrete
  • Waste glass

ASJC Scopus subject areas

  • Ceramics and Composites
  • Chemistry(all)
  • Condensed Matter Physics
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Development of a method for CO<sub>2</sub> solidification of glass and concrete waste composites'. Together they form a unique fingerprint.

Cite this