Determination of rhombohedral structure of BiFeO3 single-domain-like films grown on SrTiO3 and LaAlO3 substrates by X-ray diffraction using ð213Þhex

Tomohiro Ichinose, Shintaro Yasui, In Tae Bae, Hiroshi Naganuma

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

The crystal structure of bismuth ferrite (BiFeO3; BFO) epitaxial films was analyzed by X-ray diffraction (XRD) using a two-dimensional detector. The diffraction spots ð213Þhex (hexagonal notation was used for the rhombohedral structure in this study) specific to the rhombohedral structure (space group: R3c), which clearly separated from the diffractions in other crystal symmetries of BFO, was used for determining the crystal symmetry. The BFO films on the SrTiO3 substrates were unambiguously identified as R3c with the ð213Þhex diffraction spot, whereas highly strained BFO films (space group: Cm) on the LaAlO3 substrates did not show the diffraction spot. The structure of a single-domain-like sample with R3c could not be determined using variants, i.e., degrees of freedom for crystal orientation, whereas the Bragg's diffraction of ð213Þhex can be used to unambiguously distinguish R3c from other space groups. It was proposed that electron diffraction complemented by nondestructive and high-resolution XRD is highly effective to obtain wide-area reciprocal space information for identifying low-symmetric-complex materials such as BFO.

Original languageEnglish
Article number0902BC
JournalJapanese journal of applied physics
Volume57
Issue number9
DOIs
Publication statusPublished - 2018 Sep

ASJC Scopus subject areas

  • Engineering(all)
  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Determination of rhombohedral structure of BiFeO<sub>3</sub> single-domain-like films grown on SrTiO<sub>3</sub> and LaAlO<sub>3</sub> substrates by X-ray diffraction using ð213Þ<sub>hex</sub>'. Together they form a unique fingerprint.

  • Cite this