Dependence of ion implantation: Induced defects on substrate doping

Kei Kanemoto, Fuminobu Imaizumi, Tatsufumi Hamada, Yukio Tamai, Akira Nakada, Tadahiro Ohmi

Research output: Contribution to journalArticlepeer-review

3 Citations (Scopus)

Abstract

The characteristics of an ion implantation-induced defect in a silicon substrate are investigated. This defect is considered to be a complex of a point defect and a substrate dopant atom. The experiments are conducted by focusing on the dependence of the substrate dopant species (phosphorus and boron) on defect formation. The characteristics of the defect are investigated by measuring the bulk generation lifetime (τg) of metal-oxide-semiconductor capacitors, in which Si+ has been implanted to form the dopant-related defects in the substrate (damaging implantation) after gate oxide formation. As a result, it is found that the τg of the boron-doped substrate is one to two orders of magnitude smaller than that of the phosphorus-doped substrate for the same Nsub under the same implantation conditions. The temperature dependence of τg shows that the energy level of the defect is located at the intrinsic Fermi level, independent of the substrate dopant species and the concentration. By measuring the dependence of τg on the temperature of postdamaging implantation annealing, it is shown that the defects vanish at about 800 °C for both types of substrate. Also, it is found that the amount of dopant-related defects depends on the implantation ion species. BF+2 implantation forms more defects than As' implantation.

Original languageEnglish
Pages (from-to)3156-3161
Number of pages6
JournalJournal of Applied Physics
Volume89
Issue number6
DOIs
Publication statusPublished - 2001 Mar 15

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Fingerprint

Dive into the research topics of 'Dependence of ion implantation: Induced defects on substrate doping'. Together they form a unique fingerprint.

Cite this