Degradation of yttria stabilized zirconia at 370 K under a low applied stress

Junguo Li, Lianmeng Zhang, Qiang Shen, Toshiyuki Hashida

Research output: Contribution to journalArticlepeer-review

27 Citations (Scopus)

Abstract

The tetragonal-to-monoclinic phase transformation in ZrO2-3mol.%Y2O3 containing 0-5% Al2O3 during aging in hot water (370 K) under 100 MPa stress is investigated. It is found that while a small tensile stress accelerates the degradation, a compressive stress has little affect on the degradation. The degradation of PSZ under tensile stress is considered to be caused by the reaction between Y2O3 and H2O. Small amount of Al2O3 addition does not change the degradation mechanism of PSZ, but it prevents further continuation of degradation when the transformed volume reaches a certain value.

Original languageEnglish
Pages (from-to)26-30
Number of pages5
JournalMaterials Science and Engineering A
Volume297
Issue number1-2
DOIs
Publication statusPublished - 2001 Jan 15

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Degradation of yttria stabilized zirconia at 370 K under a low applied stress'. Together they form a unique fingerprint.

Cite this