Deformation behavior of Mg–5Y–2Nd–0.5Zr alloys with different Sm additions

Yunwei Gui, Yujie Cui, Huakang Bian, Quanan Li, Lingxiao Ouyang, Akihiko Chiba

Research output: Contribution to journalArticlepeer-review

1 Citation (Scopus)

Abstract

Herein, we studied the microstructural evolution and deformation behavior of aged Mg–5Y–2Nd–xSm–0.5Zr (x = 1, 3, and 5 wt%) alloys during uniaxial compression at room temperature by transmission electron microscopy and quasi-in-situ electron backscatter diffraction techniques. The microstructures of Mg–5Y–2Nd–xSm–0.5Zr alloys are refined by the addition of Sm, with more occurrences of Mg(Nd, Sm) precipitates. The average grain size decreased significantly with increasing Sm content, from 80.4 µm (1 wt% Sm) to 64.8 µm (3 wt% Sm) and 50.0 µm (5 wt% Sm). The Mg–5Y–2Nd–3Sm–0.5Zr alloy exhibited a maximum compressive strength of 390.1 MPa and a maximum strain (ε) of 0.103 at room temperature; {10−12} tensile twinning and dislocation slips are the main plastic deformation modes of Mg–5Y–2Nd–xSm–0.5Zr alloys during compression at room temperature. A number of<a>and<c + a>dislocations were observed in the aged Mg–5Y–2Nd–3Sm–0.5Zr alloy. The optimized ductility value is attributable to grain refinement; elemental Sm promotes the activation of the non-basal<c + a>slip dislocations and interactions between twins and<c + a>dislocations. The strengthening mechanism mainly includes solid solution, fine-grain, and precipitation strengthening.

Original languageEnglish
Article number158201
JournalJournal of Alloys and Compounds
Volume856
DOIs
Publication statusPublished - 2021 Mar 5

Keywords

  • Dislocation
  • Mg–RE alloy
  • Precipitate
  • Sm
  • Twinning

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Deformation behavior of Mg–5Y–2Nd–0.5Zr alloys with different Sm additions'. Together they form a unique fingerprint.

Cite this