Cu-Hf-Ti-Ag-Ta bulk metallic glass composites and their properties

Zan Bian, Hidemi Kato, Chunling Qin, Wei Zhang, Akihisa Inoue

Research output: Contribution to journalArticlepeer-review

92 Citations (Scopus)

Abstract

Multi-component (Cu0.50Hf0.35Ti0.10Ag 0.05)100 - xTax (x = 0, 1, 3, 5, 8, 12) bulk metallic glass (BMG) composites containing in situ formed dendrites were prepared successfully. With increasing Ta content, both compressive fracture strength (σf) and elastic-plastic strain (εf) increase from 2180 MPa and 2.1% for x = 0, to 2770 MPa and 19.2% for x = 8, respectively, but yield strength and elastic modulus decrease. The precipitation of a high volume fraction of the dendrites (Vdendrite) causes the compositional variation of the dendrites and its counterpart glass matrix. Composition analysis shows that both Hf and Ti elements exhibit an opposite behavior of dissolving into the dendrites during the cooling. About 7-11 at.% component elements (Ti, Cu and Ag) were detected in Ta-rich dendrites, but no Hf element was found. With increasing Vdendrite, the content of component elements dissolving into Ta-rich dendrites decreases from 11.35 at.% for Vdendrite = 4.3% and 7.97 at.% for Vdendrite = 26.5%. Indentation testing was also performed to evaluate the properties of the composites. With increasing Vdendrite, the hardness of the dendrites decreases from 6.0 GPa for x = 3 to 5.21 GPa for x = 12, and its elastic modulus increases from 151.2 GPa for x = 3 to 156.9 GPa for x = 12. The hardness and elastic modulus of the glassy matrix also decrease, respectively, from 9.66 and 148.7 GPa for x = 0 to 9.36 and 137.4 GPa for x = 12 with increasing precipitation of the dendrites. The variation of the properties is due to the compositional change originating from the opposite behavior of Hf and Ti elements to dissolve into the dendrites.

Original languageEnglish
Pages (from-to)2037-2048
Number of pages12
JournalActa Materialia
Volume53
Issue number7
DOIs
Publication statusPublished - 2005 Apr

Keywords

  • Bulk metallic glass composite
  • Composition
  • Dendrite
  • Indentation
  • Mechanical property

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Polymers and Plastics
  • Metals and Alloys

Fingerprint

Dive into the research topics of 'Cu-Hf-Ti-Ag-Ta bulk metallic glass composites and their properties'. Together they form a unique fingerprint.

Cite this