Cryogenic fracture toughness and temperature rise of thick section weldment in forged JJ1 type austenitic stainless steel plate

Yasuhide Shindo, Tomotaka Takahashi, Katsumi Horiguchi, Tomoyuki Kobori, Kazuaki Sanada

Research output: Contribution to journalArticlepeer-review

1 Citation (Scopus)

Abstract

JJ1 type austenitic stainless steel is emerging as the preferred structural material for superconducting magnet casings to operate at liquid helium temperature (4K). In order to evaluate the cryogenic fracture toughness and the temperature rise of tangsten inertgas (TIG) weld in 200 mm thick forged JJ1 type austenitic stainless steel plate for fusion reactor magnets of the next generation, elastic-plastic fracture toughness (Jic) tests were performed with 1T compact tension specimens at 4K. Testing was conducted in accordance with ASTM standards E813 87 for determining Jic using the unloading compliance technique to monitor crack growth. Au/0.07% Fe -Chromel thermocouples were used to measure the temperature rise near the crack tip. The effects of specimen location and nitrogen content on Jic are examined. Specimens were subjected to scanning electron microscopy (SEM) after fracture testing. The effect of inclusion content on the elastic-plastic fracture toughness parameters (Jq, Jic) is also discussed using optical microscopy and energy dispersive X-ray spectrometer (EDX).

Original languageEnglish
Pages (from-to)370-375
Number of pages6
JournalYosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society
Volume15
Issue number2
DOIs
Publication statusPublished - 1997 May

Keywords

  • Austenitic Stainless Steels
  • Compact Tension Specimens
  • Cryomechanics
  • Fracture Mechanics
  • Fracture Toughness
  • Temperature Rise
  • Unloading Compliance Method
  • Weldments

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Surfaces, Coatings and Films
  • Metals and Alloys

Fingerprint Dive into the research topics of 'Cryogenic fracture toughness and temperature rise of thick section weldment in forged JJ1 type austenitic stainless steel plate'. Together they form a unique fingerprint.

Cite this