Conduction properties and ionic transference behavior of CaTi 1-xScxO3-δ (x=0.05, 0.1)

H. J. Hong, K. Yashiro, S. Hashimoto, T. Kawada

Research output: Contribution to journalArticle

7 Citations (Scopus)

Abstract

Sc doped CaTiO3, CaTi1-xScxO 3-δ (x=0.05, 0.1) was fabricated by a solid state reaction method and their conduction properties were investigated systematically using a 4-terminal method at various temperatures (500oC to 1000oC) and oxygen partial pressures. Oxygen partial pressure dependence of the conductivity was analyzed from a defect chemical point of view in order to estimate the ionic and the electronic partial conductivities. The ionic conductivity of CaTi 1-xScxO3-δ for x=0.05 and 0.1 were 0.018 S.cm-1 and 0.033 S.cm-1, respectively at 1000oC, and their ionic transference numbers were higher than 0.90 under SOFC operating condition. The both CaTi1-xScxO3-δ showed higher ionic conductivity than 8YSZ at measured temperature ranges. From these results, CaTi1-xScxO3-δ (x=0.05, 0.1) has high potential for alternative electrolyte materials of SOFCs, especially for ITSOFCs.

Original languageEnglish
Pages (from-to)151-157
Number of pages7
JournalECS Transactions
Volume61
Issue number1
DOIs
Publication statusPublished - 2014

ASJC Scopus subject areas

  • Engineering(all)

Fingerprint Dive into the research topics of 'Conduction properties and ionic transference behavior of CaTi <sub>1-x</sub>Sc<sub>x</sub>O<sub>3-δ</sub> (x=0.05, 0.1)'. Together they form a unique fingerprint.

  • Cite this