Cobalt-bilayer catalyst decorated Ta3N5 nanorod arrays as integrated electrodes for photoelectrochemical water oxidation

Jungang Hou, Zheng Wang, Chao Yang, Huijie Cheng, Shuqiang Jiao, Hongmin Zhu

Research output: Contribution to journalArticlepeer-review

81 Citations (Scopus)

Abstract

Ta3N5 nanorod arrays were fabricated by nitridation of fluorine-containing tantalum oxide (F-Ta2O5) nanorod arrays grown in situ on Ta substrates by a one-pot vapour-phase hydrothermal induced self-assembly technique. In this protocol, the in situ generation and the morphology of arrays elaborately adjusted by reaction time, play a vital role in the formation of the F-Ta2O5 nanorod arrays and a highly conductive interlayer between the nanorods and the substrate. Due to the shape anisotropy, ordered hierarchical structure and high surface area, a high photoelectrochemical activity was achieved by the optimum Ta3N 5 nanorod photoelectrode with a photocurrent density of 1.22 mA cm-2 under AM 1.5G irradiation at 1.23 V vs. RHE (reversible hydrogen electrode). Furthermore, a higher and more stable photocurrent was demonstrated by combining the highly active Ta3N5 nanorods with stable Co3O4/Co(OH)2 (Co3O 4/Co(ii)) bilayer catalysts when compared with that demonstrated for Co(ii)/Ta3N5 and Co3O4/Ta 3N5 photoelectrodes, exhibiting that not only is the onset potential negatively shifted but also the photocurrent and the stability are significantly improved, which is correlated to an order of magnitude reduction in the resistance to charge transfer at the Ta3N5/H 2O interface. Specifically, about 92% of the initial stable photocurrent remains after long-term irradiation at 1.23 V vs. RHE. At 1.23 V vs. RHE, the photocurrent density of Co3O4/Co(ii)/Ta 3N5 arrays reached 3.64 mA cm-2 under AM 1.5G simulated sunlight at 100 mW cm-2, and a maximum IPCE of 39.5% was achieved at 440 nm. This combination of catalytic activity, stability, and conformal decoration makes this a promising approach to improve the photoelectrochemical performance of photoanodes in the general field of energy conversion.

Original languageEnglish
Pages (from-to)3322-3330
Number of pages9
JournalEnergy and Environmental Science
Volume6
Issue number11
DOIs
Publication statusPublished - 2013 Nov 1
Externally publishedYes

ASJC Scopus subject areas

  • Environmental Chemistry
  • Renewable Energy, Sustainability and the Environment
  • Nuclear Energy and Engineering
  • Pollution

Fingerprint Dive into the research topics of 'Cobalt-bilayer catalyst decorated Ta<sub>3</sub>N<sub>5</sub> nanorod arrays as integrated electrodes for photoelectrochemical water oxidation'. Together they form a unique fingerprint.

Cite this