Characterization of ultrafine SiC-Si3N4 composite powder after heat-treatment in Ar + N2

Xingguo Li, Akihiko Chiba, Yoshinori Nakata, Hideaki Nagai, Masaaki Suzuki

Research output: Contribution to journalArticlepeer-review

15 Citations (Scopus)

Abstract

Ultrafine SiC-Si3N4 composite powder synthesized by laser-induced gas-phase reaction was heat-treated at a temperature range of 295-1773 K in a mixture gas flow of Ar + N2. The changes in crystalline structure, shape, particle size, crystalline size, chemical composition, specific surface area and defect state were investigated by X-ray diffraction (XRD), transition electron microscope, chemical analysis, specific surface area analysis and electron spin resonance. No significant changes in the structure are observed after the heat treatment below 1673 K in Ar + N2, similar to the result of the heat-treatment in Ar. At or above 1673 K, the characteristic changes occur, but these depend on the heating atmosphere. The precipitation of metallic silicon, which is observed in the heat-treatment in Ar, is suppressed by introducing only 5% N2 to the atmosphere. The composite powder with a desired composition of SiC and Si3N4 can be obtained by adjustment of the nitrogen partial pressure.

Original languageEnglish
Pages (from-to)95-101
Number of pages7
JournalMaterials Science and Engineering A
Volume219
Issue number1-2
DOIs
Publication statusPublished - 1996 Nov 30
Externally publishedYes

Keywords

  • Crystalline structure
  • Heat treatment
  • X-ray diffraction

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Characterization of ultrafine SiC-Si<sub>3</sub>N<sub>4</sub> composite powder after heat-treatment in Ar + N<sub>2</sub>'. Together they form a unique fingerprint.

Cite this