Characterization of oxidation of green rust (CI-) containing copper in aqueous solution

Futoshi Nagata, Katsuya Inoue, Kozo Shinoda, Ingo Bergmann, Vladimir Šepelák, Shigeru Suzuki

Research output: Contribution to journalArticle

5 Citations (Scopus)

Abstract

To clarify the role of Cu in the oxidation of green rust (GR(C -)), which contains Fe(II) and Fe(III) ions, Cu-containing GR(Cl -) suspensions were synthesized and oxidized under various reaction conditions using nitrogen gas containing oxygen as the oxidant. X-ray diffraction (XRD) measurements were performed for analyzing the solid particles formed in the synthesis and oxidation steps. Upon the addition of Cu ions, a part of GR(Cl-) was oxidized to Fe3O4, while the Cu ions were reduced to metallic Cu (Cu(0)) in the GR(Cl-) suspensions. The pH and oxidation-reduction potentials (ORPs) of the aqueous solutions were measured during oxidation. The results showed that after oxidation, the pH of the solutions decreased, while the ORP increased. After the introduction of oxygen, GR(Cl-) was converted to iron oxides such as γ-FeOOH, α-FeOOH, and Fe3O4. The rate of conversion of GR(Cl-) to Fe3O4 was enhanced after the addition of Cu ions. The oxidation processes of the GR(Cl4) suspension containing copper revealed a reaction process in the ORP curve, which may be attributed to the reaction of Cu(0)/Cu(II) in the aqueous solution.

Original languageEnglish
Pages (from-to)2557-2562
Number of pages6
JournalMaterials Transactions
Volume50
Issue number11
DOIs
Publication statusPublished - 2009 Nov 1

Keywords

  • Copper
  • Green rust
  • Iron
  • Oxidation
  • Reduction
  • X-ray diffraction

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Characterization of oxidation of green rust (CI<sup>-</sup>) containing copper in aqueous solution'. Together they form a unique fingerprint.

  • Cite this