Characterization of heating and nitriding processes of titanium thin films grown on NaCl (001) substrate held at room temperature

Y. Kasukabet, Y. Watanabe, S. Yamamoto, M. Yoshikawa, Y. Fujino

Research output: Contribution to journalArticlepeer-review

Abstract

Both hcp-Ti and CaF2-type TiHx (x ∼ 1.5) with preferred orientations have been grown in as-deposited Ti flims on NaCl (001) substrates held at room temperature (RT). In order to clarify atomistic growth processes of TiNy films due to the implantation of nitrogen ions (N2 +) with 62 keV into Ti films, changes of the crystallographic and electronic structures of Ti thin films by heating and by nitriding during N-implantation were investigated by in-situ transmission electron microscope (TEM) observations combined with electron energy loss spectroscopy (EELS), with the aid of molecular orbital calculations. H atoms which constituted TiHx in the as-deposited Ti films were released with heating up, and were completely released at 350°C. The H-released unstable fcc-Ti sublattice was then epitaxially transformed into hcp-Ti. The loss peak observed by EELS for TiHx shifted to the lower energy side with the decrease in the electron density in the hybridised valence band due to the release of H atoms from TiHx during heating. On the other hand, the TiNy was epitaxially formed by the N-implantation into the hcp-Ti, through the transformation of the hcp-Ti to fcc-Ti sublattice, partially inheriting the atomic arrangement of the hcp-Ti and accompaNying the occupation of O-sites of the fcc-Ti by N atoms. The loss peak during N-implantation into the hcp-Ti films gradually shifted to the higher energy side with the increase in dose, due to the increase in the electron density in the hybridised valence band. Taking into account the bonding interaction of Ti sublattices with ligand H or N atoms, the transformation mechanisms between fcc-Ti sublattices and hcp-Ti sublattices due to the release of H atoms or due to the implantation of N atoms will be clarified.

Original languageEnglish
Pages (from-to)625-632
Number of pages8
Journale-Journal of Surface Science and Nanotechnology
Volume7
DOIs
Publication statusPublished - 2009 May 16

Keywords

  • Fcc-hcp transformation
  • In-situ TEM
  • Ion-implantation
  • TiH
  • TiN

ASJC Scopus subject areas

  • Biotechnology
  • Bioengineering
  • Condensed Matter Physics
  • Mechanics of Materials
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films

Fingerprint Dive into the research topics of 'Characterization of heating and nitriding processes of titanium thin films grown on NaCl (001) substrate held at room temperature'. Together they form a unique fingerprint.

Cite this