Characterization of Au thin films deposited on α-Sn(1 1 1)-(3×3)/InSb(1 1 1)A surfaces

Y. Kasukabe, X. Zhao, S. Nishida, Y. Fujino

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

For the purpose to elucidate the character of the interface between Au metal and α-Sn films, Au metal thin films deposited on α-Sn(1 1 1) surfaces grown on InSb(1 1 1)A substrates are examined by using reflection high-energy electron diffraction (RHEED). The (1 1 1) surface of the α-Sn film with only the 3×3 reconstruction grown at 50 °C is used as a well-defined α-Sn(1 1 1) substrate for the growth of Au films. NiAs-type AuSn films with a high crystallinity are grown in the 1.1-nm-thick Au-deposited thin films on the α-Sn(1 1 1) held at room temperature (RT). The NiAs-type AuSn films have a 2×2 reconstructed surface structure. The orientation relationships between the AuSn and the α-Sn films are (0 0 1) AuSn//(1 1 1) α-Sn and [2 1 0]AuSn//[2 over(1, -) over(1, -)] α-Sn. On the other hand, at 60 °C, the AuSn with a high crystallinity grows in Au-deposited films of about 2.8 nm in thickness, although at RT the AuSn with a high crystallinity grows in Au-deposited films of about 1.1 nm in thickness as stated above. The difference of Au-deposited film thickness between them results from the difference of their interdiffusion lengths of Au and Sn atoms, which depend on the temperature. Taking the interdiffusion into account, the properties and the formation mechanism of interfaces between Au metal thin films as an electrode and the α-Sn/InSb semiconductor superlattice are discussed.

Original languageEnglish
Pages (from-to)394-399
Number of pages6
JournalJournal of Crystal Growth
Volume301-302
Issue numberSPEC. ISS.
DOIs
Publication statusPublished - 2007 Apr 1

Keywords

  • A1. Crystal structure
  • A1. Reflection high-energy electron diffraction
  • A1. Surface structure
  • A3. Molecular beam epitaxy
  • B1. Alloys

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Inorganic Chemistry
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Characterization of Au thin films deposited on α-Sn(1 1 1)-(3×3)/InSb(1 1 1)A surfaces'. Together they form a unique fingerprint.

  • Cite this