Atmosphere dependence of the frictional wearing properties of partly-polished polycrystalline diamonds

H. Miki, N. Yoshida, K. Bando, T. Takeno, T. Abe, T. Takagi

Research output: Contribution to journalArticlepeer-review

14 Citations (Scopus)

Abstract

Low friction and low wear states were realized with partly-polished diamond films. Polycrystalline diamond films were deposited onto TiC substrates by microwave chemical vapor deposition using a gas mixture of CH4 and H2. The deposited diamond film was polished with each other up to a surface roughness Ra = 0.25 μm. A newly developed pin-on-disk examination method was proposed in order to realize sliding between parallel flat surfaces without misalignment. These pins were fabricated using one of the following metals: hard die steel, D2, and stainless steels, AISI440C, AISI420 and AISI304. Friction and wear tests were carried out in ambient air, dry air and in a nitrogen atmosphere. In the case of D2, we confirmed a very low and stable friction coefficient μ = 0.08 when the test were performed in an ambient atmosphere without the usage of lubrications. Furthermore, we obtained much lower friction coefficients in the nitrogen atmosphere. Among all metals studied, the wear volume was also very minute in the case of the hard metals of D2 and AISI440C.

Original languageEnglish
Pages (from-to)868-872
Number of pages5
JournalDiamond and Related Materials
Volume17
Issue number4-5
DOIs
Publication statusPublished - 2008 Apr

Keywords

  • Abrasion
  • Diamond film
  • Tribology
  • Wear

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Chemistry(all)
  • Mechanical Engineering
  • Materials Chemistry
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Atmosphere dependence of the frictional wearing properties of partly-polished polycrystalline diamonds'. Together they form a unique fingerprint.

Cite this