Acid Leaching Behavior of Zinc Ferrite in an Agitated Vessel

Katsutoshi Matsumoto, Shoji Taniguchi, Atsushi Kikuchi

Research output: Contribution to journalArticlepeer-review

2 Citations (Scopus)

Abstract

Leaching behaviors of synthetic zinc ferrite particles in acid solutions (HNO3, HCl and H2SO4) were studied by the use of an agitated vessel. The rate-controlling step was found to be the chemical reaction at the surface of the particle. The apparent activation energy was about 66 kJ/mol for HNO3, 92 kJ/mol for HCl, and 68 kJ/mol for H2SO4, respectively. Only in some cases of leaching with HNO3 solution, did the leaching rate appear to decrease with time. In that case, a nonstoichiometric dissolution with a preferred dissolution of zinc was observed. This phenomenon is more pronounced at high temperatures and high agitation speeds. Scanning Electron Microscope observations showed that the particles agglomerated. Furthermore, the number of particles in the solution decreased during the experiments. The results of several analyses; XRD, FT-IR spectrum, EDS and EPMA, showed that there were precipitates composed of iron and nitrate between agglomerated particles. These precipitates appear to cause the nonstoichiometric dissolution and the particle agglomeration which decreases the reaction area of the particles.

Original languageEnglish
Pages (from-to)345-351
Number of pages7
JournalNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
Volume63
Issue number3
DOIs
Publication statusPublished - 1999

Keywords

  • Acid leaching
  • Agglomeration
  • Chemical reaction
  • Dissolution rate
  • Nonstoichiometric dissolution
  • Zinc ferrite
  • Zinc hydrometallurgy
  • Zinc recovery

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Acid Leaching Behavior of Zinc Ferrite in an Agitated Vessel'. Together they form a unique fingerprint.

Cite this