Abstract
In this study, the relationship between (110) grain growth and magnetic properties (coercive force Hc and the magnetic induction at 800 A/m B8) at the final-annealing was studied. It was clarified that (110) abnormal grains grew dramatically after FATIME= 0.5 min and the thin sheets with B8 ≅ 1.9 can be obtained at FATIME = 20 min. Further, it was confirmed that an increase of intermediate-annealing temperature (IAT) realizes FATIME = 1 min. to cover the sheets with only (110) grains.